 Viton® A - 66% Fluorine GOOD–Chemical Resistance General Properties Chemical Resistance: A broad range of resistance to oils, fuels, lubricants and most mineral acids. Very good resistance to many aliphatic hydrocarbon fluids that act as solvents for many other rubbers. Compression Set: Exceptionally good resistance even at temperatures that can embrittle other non-fluorinated elastomers. Environmental: Good resistance to atmospheric oxidation, sun, and weather, excellent resistance to fungus and mold. General PurposeViton® Fluoroelastomer Thermodyn Sheeting TH-1270-40C made with Viton® ASTM D2000 specifications 2HK707B38E078Z Branded Sheet meets ASTM D2000 specifications 2HK707B38E078Z • Guarantees highest quality commercial sheeting available for gaskets. • Fully certifiable to ASTM D2000. • Eliminates inventory confusion • Hardness Durometer: 75±5 • Tensile Strength: <1600psi • Elongation: 165% • Temperature Range: -18°C to 204°C (400°F) • 100% Virgin Viton® Compound • Compression Set, ASTM D395B plied: 50% maximum Discs. 22hr @ 175°C Additional Products made with Viton® A Commerical Grade TD-70C / TH-1270 Military Specifications • MIL-R-83248-2 Type 11, Class 1 U.S. Governmental Qualified Q.P.L.-83248-2 3953-MLS95-009 • MIL-R-83248, Type 11, Class 11 • FDA Approved White and Black • Fiberglass and Nomex® reinforced gasket sheeting. • Valve Diaphragm material • Custom Colors Available • Smooth and Fabric finish available. • Standard widths 36" and 48". • Custom widths up to 59"±1" • Diaphragm Sheeting • All products can be made to metric sizes Stock Products • TD-70C / TH-1270 • FDA white and black • Mil spec 75 + 90 duro • TH-55 duro Commercial • TH-90 duro Commercial |
|
 Home | About Us | Capabilities | Expansion Joints and Materials | Gasket Materials | Caulks & Coatings | Molded Rubber Products | Contact Us © Copyright 1998-2004 Thermodyn Corporation. All rights reserved |
||